Anti-Reflection Property of SiO 2 Composite Films for Solar Cell
Yazarlar (2)
Doç. Dr. Hafize Nagehan KÖYSÜREN Kırşehir Ahi Evran Üniversitesi, Türkiye
Prof. Dr. Özcan Köysüren Ankara Üniversitesi, Türkiye
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | Journal of Macromolecular Science Part B Physics (Q4) | ||
| Dergi ISSN | 0022-2348 Wos Dergi Scopus Dergi | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 10-2024 |
| Cilt / Sayı / Sayfa | 65 / 2 / 250–260 | DOI | 10.1080/00222348.2024.2414582 |
| Makale Linki | https://doi.org/10.1080/00222348.2024.2414582 | ||
| Özet |
| In this study, anti-reflection property of SiO2 based composite films were investigated. For this purpose, SiO2/TiO2, SiO2/ZnO and SiO2/TiO2/ZnO composite films were prepared using a sol-gel technique and coated on glass slides. Polyethylene glycol (PEG) with molecular weight of 1500 g/mol was inserted into the SiO2 composite film as a porogen to decrease the refractive index and improve the anti-reflection property of the as-prepared film. The SiO2 films with pore structures were successfully obtained. The PEG modified SiO2/ZnO (SiO2/PEG/ZnO) film provided a water contact angle close to the water contact angle of a superhydrophilic surface. In addition, the SiO2/PEG/ZnO film exhibited the highest average transmittance of 92.7% higher than that of the uncoated glass slide. The photovoltaic conversion efficiency of the solar cell coated with the SiO2/PEG/ZnO film was very close to that of the solar cell without … |
| Anahtar Kelimeler |
| anti-reflection coating | PEG | SiO2 | solar cell | TiO2 | ZnO |