Effects of cold and warm temperatures on springback of aluminium-magnesium alloy 5083-H111
Yazarlar (4)
F. Ozturk
Niğde Ömer Halisdemir University, Türkiye
Niğde Ömer Halisdemir University, Türkiye
S. Toros Niğde Ömer Halisdemir University, Türkiye
Prof. Dr. Süleyman KILIÇ Niğde Ömer Halisdemir University, Türkiye
M. H. Bas
Niğde Ömer Halisdemir University, Türkiye
Niğde Ömer Halisdemir University, Türkiye
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | Proceedings of the Institution of Mechanical Engineers Part B Journal of Engineering Manufacture (Q3) | ||
| Dergi ISSN | 0954-4054 Dergi Bilgileri (2009) | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 01-2009 |
| Cilt / Sayı / Sayfa | 223 / 4 / 427–431 | DOI | 10.1243/09544054JEM1335 |
| Makale Linki | http://dx.doi.org/10.1243/09544054jem1335 | ||
| UAK Araştırma Alanları |
Üretim Teknolojileri
|
||
| Özet |
| Springback is one of the most common problems in sheet metal forming processes. It causes improper fit, which creates serious problems during assembly of the parts. Based on material strength, a considerable amount of elastic recovery during unloading can be observed. In this study, springback behaviour of a hardened 5083-H111 aluminium-magnesium (Al—Mg) alloy with a thickness of 3 mm using a 60°angle V-shape die bending process at various temperatures ranging from -50 to 300 °C was investigated. The effects of temperature on springback behaviour were identified. Results indicate that springback increased with decreasing temperature. The same amount of springback was measured at 0, 25, and 100 °C. It was observed that the amount of springback increased between 100 and 200 °C and then started to decrease beyond 200 °C. The lowest springback was obtained at 300 °C. |
| Anahtar Kelimeler |
| 5083-H111 aluminium-magnesium alloy | Springback | V-bending | Warm forming |
Science Direct
Effects of cold and warm temperatures on springback of aluminium-magnesium alloy 5083-H111