Polyphosphazene based Composite Polymer Electrolytes
Yazarlar (6)
| Bildiri Türü | Tebliğ/Bildiri |
| Bildiri Alt Türü | Özet Metin Olarak Yayınlanan Tebliğ (Uluslararası Kongre/Sempozyum) |
| Bildiri Niteliği | Web of Science Kapsamındaki Kongre/Sempozyum |
| DOI Numarası | 10.1016/j.ssi.2006.05.003 |
| Bildiri Dili | İngilizce |
| Kongre Adı | International Conference on Solid State Ionics (SSI-15) |
| Kongre Tarihi | 17-07-2005 / 22-07-2005 |
| Basıldığı Ülke | Almanya |
| Basıldığı Şehir | Baden-Baden |
| Özet |
| Composite salt-in-polymer electrolyte membranes were prepared from poly[(bis(2-methoxyethyl)amino)(1-x)(n-propylamino)(x)-phosphazene] (BMEAP) with dissolved LiCF3SO3 and dispersed Al2O3 nanoparticles (40 run). Membranes with good mechanical stability were obtained. Low ionic conductivities were found in particle free membranes with maximum conductivities at 10 wt.% LiCF3SO3 ranging from 3.1 x 10(-7) S/cm at 30 degrees C to 1.8 x 10(-5) S/cm at 90 degrees C. For the composite membranes, addition of 2 wt.% Al2O3 nanoparticles leads to a steep increase of the conductivity by almost two orders of magnitude as compared to the homogeneous membranes. The highest room temperature conductivity for the investigated BMEAP-LiCF3SO3-Al2O3 composite systems was 10(-5) S/cm. (c) 2006 Elsevier B.V. All rights reserved. |