Synthesis of Cross Linked Comb Polysiloxane for Polymer Electrolyte Membranes
Yazarlar (4)
Prof. Dr. Yunus KARATAŞ University Of Münster, Almanya
Nitin Kaskhedikar
University Of Münster, Almanya
University Of Münster, Almanya
Marina Burjanadze
University Of Münster, Almanya
University Of Münster, Almanya
Hans Dieter Wiemhöfer
University Of Münster, Almanya
University Of Münster, Almanya
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | Macromolecular Chemistry and Physics | ||
| Dergi ISSN | 1022-1352 Wos Dergi Scopus Dergi | ||
| Dergi Tarandığı Indeksler | SSCI | ||
| Makale Dili | İngilizce | Basım Tarihi | 02-2006 |
| Kabul Tarihi | 12-04-2026 | Yayınlanma Tarihi | – |
| Cilt / Sayı / Sayfa | 207 / 4 / 419–425 | DOI | 10.1002/macp.200500470 |
| Makale Linki | http://doi.wiley.com/10.1002/macp.200500470 | ||
| Özet |
| Summary: A series of comb‐like polysiloxanes was prepared as the base polymer for solvent‐free polymer electrolyte membranes. Hydrosilylation of poly(methylhydrosiloxane) (PMHS) was used to substitute hydrogen by the two types of side groups tetraethylene glycol allyl methyl ether and allyltrimethoxysilane (ATMS) with varying molar ratios between 5 and 40 mol‐% ATMS. The ATMS side groups served to cross‐link as‐prepared polymer electrolyte membranes after dissolving lithium trifluoromethylsulfonate (triflate) or lithium bis(trifluoromethylsulfonyl)imide. The ionic conductivities of these salt‐in‐polymer membranes prepared with a constant concentration of 10 wt.‐% lithium triflate showed a maximum conductivity of 4.6 × 10−5 S · cm−1 at 30 °C for 10 mol‐% ATMS substitution. In another series of experiments with the ATMS substitution held constant at 10 mol‐%, the salt concentration was varied … |
| Anahtar Kelimeler |
| Comb polymer | Hydrosilylation | Polymer electrolyte | Polysiloxanes | Salt-in-polymer | Synthesis |