| Özet |
| Proton conducting membranes have been prepared using sulfonated poly[bis(phenoxy)phosphazene] (s-BPP) trapped in a cross-linked interpenetrating hydrophilic network of hexa(vinyloxyethoxyethoxy)cyclotriphosphazene (CVEEP). Membranes with good mechanical and thermal stabilities were obtained exhibiting high ion exchange capacities in the range of 1.62-1.79 mmol/g. The proton conductivity was measured as a function of water partial pressure in nitrogen (0 mbar to 25 mbar) in the temperature range 25 °C to 75 °C. At 25 mbar water partial pressure and 75 °C, a conductivity of 2.2 × 10- 4 S/cm was obtained for s-BPP with a network made of 50 wt.% CVEEP. After immersion in water, the conductivity increased up to 0.013 S/cm at 25 °C. The hydrophilic nature of the CVEEP network stabilizes the water content and enhances the proton conductivity at elevated temperatures. © 2006 Elsevier B.V. All rights reserved. |
| Anahtar Kelimeler |
| Cyclophosphazene | Interpenetrating network | Polymer electrolyte | Proton conducting membrane | Sulfonated poly[bis(phenoxy)phosphazene] |
| Makale Türü | Özgün Makale |
| Makale Alt Türü | SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale |
| Dergi Adı | Solid State Ionics |
| Dergi ISSN | 0167-2738 Wos Dergi Scopus Dergi |
| Dergi Tarandığı Indeksler | SSCI |
| Makale Dili | İngilizce |
| Basım Tarihi | 10-2006 |
| Cilt No | 177 |
| Sayı | 26 |
| Sayfalar | 2425 / 2430 |
| Doi Numarası | 10.1016/j.ssi.2006.05.007 |
| Makale Linki | http://linkinghub.elsevier.com/retrieve/pii/S0167273806002864 |
| Atıf Sayıları | |
| WoS | 17 |
| SCOPUS | 20 |
| Google Scholar | 27 |