Effect of The Filler Type and Particle Distribution Changes on Polyester Matrix Composites
Yazarlar (2)
Dr. Öğr. Üyesi Şevki EREN
Kırşehir Ahi Evran Üniversitesi, Türkiye
Düzce Üniversitesi, Türkiye
| Makale Türü |
Özgün Makale
(Ulusal alan endekslerinde (TR Dizin, ULAKBİM) yayınlanan tam makale)
|
||
| Dergi Adı | Sakarya Üniversitesi Fen Bilimleri Enstitüsü Dergisi | ||
| Dergi ISSN | 1301-4048 Scopus Dergi | ||
| Dergi Tarandığı Indeksler | TR DİZİN | ||
| Makale Dili | İngilizce | Basım Tarihi | 08-2021 |
| Cilt / Sayı / Sayfa | 25 / 4 / 1009–1019 | DOI | 10.16984/saufenbilder.781256 |
| Makale Linki | http://dx.doi.org/10.16984/saufenbilder.781256 | ||
| Özet |
| In this study, the effect of the usage of additives at different initiator ratios as well as the usage of fillers of different types and different grain distributions on resin consumption and compressive strength of polyester matrix composites were investigated. Orthophthalic unsaturated polyester resin (UP) was used as a matrix. The initiator (methyl ethyl ketone peroxide) at the ratio of 1.0%, 1.5%, and 2.0% and the accelerator (cobalt octoate) at the ratio of 1.0% by weight was used to start the polymerization. Silica, basalt, and quartz sand were used as the filler type. All fillings used in the study were prepared in the grain size distribution of the American Foundry Society (AFS 40-45) and in the grain size distribution determined by reference to the Fuller equation (F 1.0). Resin consumption and pressure resistances of produced composites were determined, and SEM analyses were carried out. As a result of the study, in all filled composites, the minimum resin consumption was achieved at a starting rate of 1.0%. The highest compressive strength was determined as 130.43 MPa in the basalt filled composite and in the AFS40-45 grain distribution. |
| Anahtar Kelimeler |
| American foundry society | filler grain distribution | fuller equation | Polyester matrix composites | resin consumption |