| Özet |
| Metallic magnesium was produced by the reaction of aluminum powder with magnesium oxide in an electric arc furnace. This process was performed with calcium magnesium aluminate flux. In the literature, other reducing agents such as silicone metal and carbide were used for reduction of magnesium. In this study, raw magnesium oxide powders were used as magnesium source, and aluminum powders were used as reducing agent to reduce magnesium oxide. Magnesium oxides, aluminum powders and calcium magnesium aluminate flux were mixed and this homogenous mixture was pressed in a mold under constant force. Afterwards, the mixture put in a graphite crucible to melt at electric arc furnace by isolated melting system. Magnesium vapor occurs during melting process was transferred to cold chamber and condensed here for solidification. Physical properties of solid magnesium powders were characterized by XRD analysis and purity of Mg powders was determined by Carbon Determination Device. |
| Anahtar Kelimeler |
| Bildiri Türü | Tebliğ/Bildiri |
| Bildiri Alt Türü | Tam Metin Olarak Yayınlanan Tebliğ (Uluslararası Kongre/Sempozyum) |
| Bildiri Niteliği | Alanında Hakemli Uluslararası Kongre/Sempozyum |
| Bildiri Dili | İngilizce |
| Kongre Adı | 19th International Metallurgy & Materials Congress |
| Kongre Tarihi | 25-10-2018 / |
| Basıldığı Ülke | Türkiye |
| Basıldığı Şehir | İstanbul |